PA66 GF15 With High Tensile Strength (A2307C, A2317C) for Engineering Plastics

 PA6 6GF15 is a 15% glass fiber reinforced, toughened, polyamide 66 resin for injection molding. 

 

Typical Application of PA66 GF15 With High Tensile Strength (A2307C)

                       

PA66 15% glass fiber and high toughness modified grades are applied to the sectors of electrical switch with high tensile characteristics.

 

Processing Detail of PA66 GF15 With High Tensile Strength (A2307C)                                         

                                 

Other Details of PA66 GF15 With High Tensile Strength (A2307C)

 

Pa66 gf15 material properties                                                

Ash

(15.0% 1 ISO3451/1)

Conditioned

600°C*2h

Density

(1180Kg/m3 1 ISO1183)

Conditioned

23°C

Shrinkage Parallel Flow

(0.7-1.0 % 1 ISO294-4)

Shrinkage Vertical Flow

(1.0-1.4% I ISO294-4)

Mechanical Properties

Tensile strength (105.0MPa 1 ISO527)

Conditioned

5mm/ min

Tensile Strain at Break (2.6% I ISO527)

Conditioned

5mm/min

Notched Impact Strength (10.0 KJ/m2 I ISO179)

Conditioned

1.0J

Flexural Strength (177MPa 1ISO178)

Conditioned

2mm/min

Flexural Modulus (5050 MPa I ISO178)

Conditioned

2mm/min

Thermal Property

Melting Point

(260°C I ISO11357)

Hot Deformation Temperature

(225*C I ISO75)

Conditioned

1.8MPa

Flammability Class

(HB 1UL94)

Conditioned

mm

Injection Molding Conditions

Drying Temperature

130°C

Drying Time

3h

Cylinder Temperature

280-300°C

Nozzle Temperature

280-300*C

Tooling Temperature

80-100*C

* Molding conditions are just for reference, please make an adjustment based on the actual situation

 

As a professional engineering plastic company, Anmei group has high-quality modified plastics for sale. Welcome to contact us if needed.

 

 


Comments

Popular posts from this blog

Anmei-PA66 GF for Engineering Plastics

Anmei-Polyamide Nylon 6 (PA6) for Engineering Plastics

Transparent ABS (MABS Plastic)