PA66 GF30 (A2000F, A2011F, A2111F)



PA66 GF30 (A2000F, A2011F, A2111F) for Engineering Plastics



PA6 630GF is a polyamide 66 reinforced with 30% glass fibers. It demonstrates outstanding mechanical properties such as high fluidity, high toughness, high-temperature resistance and easy forming.



Typical Application of pa 6.6 gf30(A1000F)

The mechanical strength, creep resistance and fatigue strength of 30% reinforced Nylon66 gf30 are greatly improved, and the elongation, mold shrinkage, moisture absorption, and wear resistance are reduced. It can be injection-molded plastic parts with stressed structures in the fields of automobiles, E & E, home appliances and machinery industries.



Other Details of PA66 GF30 (A1000F)

Physical Property

Ash

(30.0% 1 ISO3451/1)

Conditioned

600°C*2h

Density

(1365Kg/m3 1 ISO1183)

Conditioned

23°C

Shrinkage Parallel Flow

(0.2-0.5 % 1 ISO294-4)

Shrinkage Vertical Flow

(0.6-0.9% I ISO294-4)

Mechanical Properties

Tensile strength (186.0MPa 1 ISO527)

Conditioned

5mm/ min

Tensile Strain at Break (2.4% I ISO527)

Conditioned

5mm/min

Notched Impact Strength (12.5 KJ/m2 IISO179)

Conditioned

1.0J

Flexural Strength (282MPa 1ISO178)

Conditioned

2mm/min

Flexural Modulus (8518 MPa I ISO178)

Conditioned

2mm/ min

Thermal Property

Melting Point

(260°C I ISO11357)

Hot Deformation Temperature

(250*C I ISO75)

Conditioned

1.8MPa

Flammability Class

(HB 1UL94)

Conditioned

mm

Injection Molding Conditions

Drying Temperature

130°C

Drying Time

3h

Cylinder Temperature

280-300°C

Nozzle Temperature

280-300*C

Tooling Temperature

80-100*C

 



As a professional masterbatch factory, Anmei provide pa6gf25, material pa66 gf30, pa4 6 gf30, heat stabilized nylon and etc. Want to know pa66 gf30 price? Contact us.

 


Comments

Post a Comment

Popular posts from this blog

PA66 GF20 (A2000D)

Image
  As an experienced plastic engineering inc  and masterbatch factory, Anmei has a professional team of senior engineers with 10-15 years of R&D experience in engineering plastics  and masterbatch, we work together to achieve our goal of solution providing and create more values for customers with our stable quality and professional technical service, making a better life for human beings.   Reinforced with 20% of glass fiber on substrate PA66 is called PA GF20 , it improves dimensionally stabilized and impact resistance for injection moulding.   Typical Application of PA66 GF   20  (A2000D) PA66 GF20 is applied to various precision gears due to its high rigidity, dimensional stability, noise reduction, wear resistance, quietness, lubrication and antistatic.   Processing Detail of PA66 GF20 (A2000D)   Other Details of PA66 GF20 (A2000D) Physical Property Ash (20.0% 1 ISO3451/1) Conditioned 600°C*2h Density (1285Kg/m3 1 ISO1183) Conditioned 23°C Shrinkage Parallel Flow (0.5-0.9 % 1 I
Read more

Antibacterial Masterbatch for Engineering Plastics

Image
  Polymer anti-bacterial masterbatch is a kind of masterbatch material that adds antibacterial agents into the carrier resin, which is offering antimicrobial protection for plastic products and reduces the growth of harmful organisms such as molds, bacteria, fungi and mildew increased rapidly on plastic surfaces.   Benefits of Antimicrobial Masterbatch Antibacterial masterbatch is an organic ingredient with good pre-dispersibility. In addition to mixed-use in the production and processing of plastic products, anti microbial masterbatch  can also be added during the production of antibacterial plastics, blended and granulated.   Antibacterial plastic is granulated by an antibacterial masterbatch , the dispersibility of an antibacterial agent in plastic is much better than antibacterial plastic blended with an antibacterial agent. Thereby, the antibacterial efficiency of the antibacterial agent is improved, the product quality is stable, and the cost of raw materials can be reduced.   Tw
Read more

Application and Types of Engineering Plastics

Image
  A pplication of P lastic in E ngineering F ield   Engineering plastics have high mechanical strength, or have good properties such as high temperature resistance, corrosion resistance, wear resistance, etc. After modification, engineering plastics are more widely used and can be used in electronics, home appliances, office equipment, communications, automobiles, water processing, electrical, aviation, military and other fields.   1. Application fields of engineering plastics Engineering plastics has become the fastest growing field in the world's plastics industry. Its development not only supports the national pillar industry and modern high-tech industry, but also promotes the transformation of traditional industries and the adjustment of product structure.   Types of engineering plastics   are increasingly used in the automotive field, mainly used in bumpers, fenders, fuel tanks, instrument panels and other interior trims, body panels, doors, lamp covers, fuel pipes, radiators
Read more