anmeiplastics

As an engineered plastics company, Anmei focuses on the production of modified engineering plastics, among which high-performance nylon 6 engineering plastics are one of our main products. We have nylon 6 modified plastics of heat-resistant, reinforced, toughened, flame-retardant, wear-resistant, weather-resistant, oil-resistant and conductive with glass fiber filling ranging from 15% to 50%. The mechanical properties of blended materials such as glass fiber and toughening agent added to nylon show that with the increase of glass fiber content, the tensile strength, impact resistance and heat resistance are better, and the bending strength has been greatly improved as well, which meet the requirements of industrial products and daily use. The polyamide 6 price that Anmei offers is very competitive. Contact us now to get more detailed information about PA6 price. Types of PA6 GF As one of engineering plastic manufacturers, we provide polyamid pa6 gf to meet the specific needs of vario

PA 66 GF 50 is a fiber-reinforced plastic made of Nylon 66 resin as a base material and 50% glass fiber as a reinforcing filler, and various processing aids be added to be used in injection molding products. Typical Application of pa6650gf (A2011J) PA66 50%GF HB grade is applied to the field of industrial product structural parts, requiring high strength, high toughness, high and low-temperature resistance, and commonly used as water valve diverter and blade of air outlet, mechanical gears and bushings. Other Details of PA66 50GF (A2011J) Physical Property Ash (50.0% 1 ISO3451/1) Conditioned 600°C*2h Density (1538Kg/m3 1 ISO1183) Conditioned 23°C Shrinkage Parallel Flow (0.1-0.3 % 1 ISO294-4) Shrinkage Vertical Flow 0.2-0.5% I ISO294-4)   Mechanical Properties Tensile strength (217.0MPa 1 ISO527) Conditioned 5mm/ min Tensile Strain at Break (2.5% I ISO527) Conditioned 5mm/min Notched Impact Strength (17.0KJ/m2 I ISO179 Conditioned 1.0J Flexural Strength (354 MPa 1ISO178) Conditioned 2

PA66 GF45 is a 45% glass fiber reinforced polyamide 6.6 with high stiffness and strength. Typical Application of PA66 GF45 (A2011I) PA66 45%GF HB grade is applied to the gear field, it requires high strength, high toughness and dynamic balance and applied to the field of sports equipment and electrical tools, it requires high toughness, low temperature resistance, and low cost. Commonly used as mechanical housing. Other Details of PA66 GF45 (A2011I) Physical Property Ash (45.0% 1 ISO3451/1) Conditioned 600°C*2h Density (1495Kg/m3 1 ISO1183) Conditioned 23°C Shrinkage Parallel Flow (0.1-0.3% 1 ISO294-4) Shrinkage Vertical Flow (0.4-0.6% I ISO294-4) Mechanical Properties Tensile strength (204.0MPa 1 ISO527) Conditioned 5mm/ min Tensile Strain at Break (2.8% I ISO527) Conditioned 5mm/min Notched Impact Strength (16.5 KJ/m2 IISO179) Conditioned 1.0J Flexural Strength (332MPa 1ISO178) Conditioned 2mm/min Flexural Modulus (13547 MPa I ISO178) Conditioned 2mm/min Thermal Property Melting

PA66 is nylon 66, namely polyamide 66. GF is glass fiber. Generally expressed as pa 6.6 gf 35, that is, 35% glass fiber is added to nylon 66. Typical Application of pa66_gf35(A2000G) It is applied to lamp holder cover and cooling fan, gears and various electronic connectors, wear-resistant parts of elevators, and internal and external structural parts around the engine such as cooling fan. Processing Detail of pa 6.6 gf35 (A2000G) Other Details of PA66 GF35 (A2000G) Physical Property Ash (35.0% 1 ISO3451/1) Conditioned 600°C*2h Density (1407Kg/m3 1 ISO1183) Conditioned 23°C Shrinkage Parallel Flow (0.2-0.4 % 1 ISO294-4) Shrinkage Vertical Flow (0.5-0.8% I ISO294-4) Mechanical Properties Tensile strength (193.0MPa 1 ISO527) Conditioned 5mm/ min Tensile Strain at Break (2.6% I ISO527) Conditioned 5mm/min Notched Impact Strength (15.0KJ/m2 IISO179) Conditioned 1.0J Flexural Strength (291MPa 1ISO178) Conditioned 2mm/min Flexural Modulus (10069 MPa I ISO178) Conditioned 2mm/ min Thermal

PA66 GF30 (A2000F, A2011F, A2111F) for Engineering Plastics PA6 630GF is a polyamide 66 reinforced with 30% glass fibers. It demonstrates outstanding mechanical properties such as high fluidity, high toughness, high-temperature resistance and easy forming. Typical Application of pa 6.6 gf30 (A1000F) The mechanical strength, creep resistance and fatigue strength of 30% reinforced Nylon66 gf30 are greatly improved, and the elongation, mold shrinkage, moisture absorption, and wear resistance are reduced. It can be injection-molded plastic parts with stressed structures in the fields of automobiles, E & E, home appliances and machinery industries. Other Details of PA66 GF30 (A1000F) Physical Property Ash (30.0% 1 ISO3451/1) Conditioned 600°C*2h Density (1365Kg/m3 1 ISO1183) Conditioned 23°C Shrinkage Parallel Flow (0.2-0.5 % 1 ISO294-4) Shrinkage Vertical Flow (0.6-0.9% I ISO294-4) Mechanical Properties Tensile strength (186.0MPa 1 ISO527) Conditioned 5mm/ min Tensile Strain at Brea