Nylon 66 PA66 Heat Stabilized (A2006X01, A2016X01)

 A range of engineering plastics produced by Anmei, one of the professional engineering plastic manufacturers, are being applied in a variety of applications of home appliances, power tool, new energy and fiber optic cable and the performance properties of these synthetic polymers can be enhanced by glass fiber, and flame retardant and toughening and heat-resistant.

 

Typical Application of Nylon66 PA66 Heat Stabilized (A2006X01)

This type of polyamide nylon 66 is used for spare parts in the automotive field, such as cable ties, pipe clamps, brackets, shells, three-way joints.

 

Processing Detail of nylon 66 tensile strength

 

Other Details of Nylon PA66 Heat Stabilized (A2006X01)

Physical Property of Heat Stabilized Nylon 6

Ash

(15.0% 1 ISO3451/1)

Conditioned

600°C*2h

Density

(1140Kg/m3 1 ISO1183)

Conditioned

23°C

Shrinkage Parallel Flow

(1.5-2.2% 1 ISO294-4)

Shrinkage Vertical Flow

(1.5-2.2% I ISO294-4)

 

Mechanical Properties of Heat Stabilized Nylon 6

Tensile strength (90.0MPa 1 ISO527)

Conditioned

50mm/min

Tensile Strain at Break (14.5% I ISO527)

Conditioned

50mm/min

Notched Impact Strength (3.3KJ/m2 I ISO179)

Conditioned

1.0J

Flexural Strength (120MPa 1ISO178)

Conditioned

2mm/min

Flexural Modulus (3026MPa I ISO178)

Conditioned

2mm/ min

 

Thermal Property of Heat Stabilized Nylon 6

Melting Point

(260°C I ISO11357)

Hot Deformation Temperature

(220*C I ISO75)

Conditioned

0.45MPa

Flammability Class

(HB 1UL94)

Conditioned

mm

 

Injection Molding Conditions of Heat Stabilized Nylon 6

Drying Temperature

90°C

Drying Time

3h

Cylinder Temperature

255-275°C

Nozzle Temperature

255-275*C

Tooling Temperature

80*C

 

* Molding conditions are just for reference, please make an adjustment based on the actual situation！

 


Comments

Post a Comment

Popular posts from this blog

Anmei-Polyamide Nylon 6 (PA6) for Engineering Plastics

Image
  Other than fiber-reinforced polyamide 6, the unreinforced nylon type 6 produced by Anmei, one of the professional nylon 6 suppliers/manufacturers, is also divided into toughened, heat-resistant, alloy and flame-retardant modified PA6.   Nylon 6 (PA 6) is made up of a group of 6 carbon atoms. PA type 6 plastic has a low melting point, a wide process temperature range, and strong impact resistance and solubility resistance. Both high tensile strength and super-high tensile strength Nylon6 (PA6) have excellent flexibility, impact resistance, low-temperature resistance, wear-resistance and dimensional stability of the nylon 6 material. PA6  material flame retardant is mainly achieved by adding halogen-free flame retardant and halogen flame retardant to achieve the flame retardant effect. The physical and mechanical properties of these nylon 6 plastic materials are comparable to similar products in Europe and America. This series of halogen-free flame retardant products comp...
Read more

PA66 GF30 Halogenated FR (A2014F, A2114F) for Engineering Plastics

Image
 PA66 GF30 FR is a Nylon 66 with 30% glass-fibers and flame retardant halogenated.  Typical Application of PA66 GF30 Halogenated FR (A2014F) The advantage of nylon 66 GF30  halogenated    pa66 fr   can maintain the original physical and chemical properties of flame retardant products. If you are interested, contact us now to get more information about Nylon pa6 gf30 price ! As one of engineering plastic manufacturers , Anmei group   provides pa6 plastic material, modified polyolefin, master batches   and etc. For more information, please feel free to contact us!
Read more

What is the Masterbatch Material in Plastic Products?

Image
  What is the Masterbatch Material in Plastic Products? Ⅰ. What is masterbatch material? Masterbatch material is a new type of special colorant for polymer materials. This superior coloring performance, energy saving, no dust and no pollution, is widely used in polyethylene, polypropylene, polystyrene, ABS, nylon, PC, PMMA, In PET and other resins, colorful fibers, clothing, daily plastics, wires and cables, household appliances, agricultural films, auto parts and other products are produced.   The   color masterbatch   is composed of three basic elements: pigments or dyes, carriers and additives. It is an aggregate obtained by uniformly loading a super-constant pigment in the resin. It can be called Pigment Concentration. The tinting strength is higher than the pigment itself. Mixing a small amount of color masterbatch and uncolored resin during processing can achieve a colored resin or product with a designed pigment concentration.   The technical requirements...